Perfluoroelastomer O-Rings
Perfluoroelastomer (FFKM) o-rings are recommended for their vast temperature range, chemical resistance in numerous aggressive applications, and long service life. Global O-Ring and Seal provides high-performance FFKM o-rings for your demanding applications. Our FFKM sealing solutions include Kalrez®, Chemraz®, and MARKEZ®.
O-ring Kalrez®
Le parti in perfluoroelastomero Kalrez® (FFKM) resistono a oltre 1.800 sostanze chimiche diverse, offrendo al contempo stabilità alle alte temperature. Sono utilizzati nei processi chimici altamente aggressivi, nella fabbricazione di wafer semiconduttori, nel settore farmaceutico, nel recupero di petrolio e gas e nelle applicazioni aerospaziali. Le prestazioni comprovate a lungo termine dei componenti Kalrez® possono significare cambi, riparazioni e ispezioni delle guarnizioni meno frequenti, aumentando i tempi di attività dei processi e delle apparecchiature per una maggiore produttività e resa.
Fare clic qui per ulteriori informazioni sui composti Kalrez® specifici.
O-ring Chemraz®
Chemraz®, l'elastomero di ultima generazione per applicazioni impegnative nei giacimenti petroliferi, offre eccellenti prestazioni di tenuta quando esposto a miscele di sostanze chimiche aggressive presenti nei pozzi ed è spesso richiesto dagli operatori. Sono stati formulati composti speciali per una migliore resistenza alla rapida decompressione del gas e all'abrasione, garantendo una significativa riduzione dei tempi di fermo e della manutenzione.
Fare clic qui per ulteriori informazioni sui composti Chemraz® specifici.
MARKEZ® O-Rings
MARKEZ® is a high-performance perfluoroelastomer (FFKM) compound line built to address very demanding sealing environments. Formulated from ingredients similar to premium FFKM brands, MARKEZ® delivers excellent chemical resistance and high temperature performance, with heat resistance up to 635°F (335°C) depending on compound selected, at outstanding value.
Click here for more information on specific MARKEZ® compounds.
| Compound | Relative Cost | Data Sheet | Hardness, (Shore A) | Tensile Strength psi, (MPa) | Elongation, %, min | Modulus at 100% psi, (MPa), min | Compression Set | Min. Temp. | Max. Temp. |
|---|---|---|---|---|---|---|---|---|---|
| General Purpose, Broad Chemical Resistance | |||||||||
| Kalrez® 6375 | $$$$$ |  |
75 | 2,200 (15.16) | 160 | 1050 (7.24) | 24 | -4ºF (-20ºC) | +527ºF (275ºC) |
| Chemraz® 505 | $$$$$ | |
75 | 1,750 (12.1) | 140 | 1310 (9.0) | 25 | -22ºF (-30ºC) | +446ºF (230ºC) |
| MARKEZ® Z1352 | $$$$ | |
77 | 2,305 (15.9) | 120 | 2,016 (13.9) | 24.7 | +5ºF (-15ºC) | +500ºF (260ºC) |
| High Temperature Resistance and Low Compression Set | |||||||||
| Kalrez® 4079 | $$$$$ | |
75 | 2,450 (16.88) | 150 | 1050 (7.24) | 14 | -2ºF (-19ºC) | +600ºF (316ºC) |
| Chemraz® 605 | $$$$$ | |
80 | 2,150 (14.8) | 130 | 1000 (6.9) | 22 | -4ºF (-20ºC) | +500ºF (260ºC) |
| MARKEZ® Z1028 | $$$$ | |
77 | 2,120 (14.7) | 165 | N/A | 20 | +5ºF (-15ºC) | +608ºF (320ºC) |
| High Temperature Resistance, Broad Chemical Spectrum, and Water/Steam Resistance | |||||||||
| Kalrez® 7075 | $$$$$ | |
75 | 2,598 (17.91) | 160 | 1629 (11.23) | 10 | 0ºF (-18ºC) | +620ºF (327ºC) |
| Chemraz® 585 | $$$$$ | |
80 | 1,825 (12.6) | 165 | 1240 (8.5) | 35 | -22ºF (-30ºC) | +428ºF (220ºC) |
| MARKEZ® Z1400 | $$$$ | |
74 | 2,742 (18.91) | 218 | N/A | N/A | +5ºF (-15ºC) | +635ºF (335ºC) |